Gray Resin - Zortrax Basic - 500 ml - Inkspire

Gray Resin - Zortrax Basic - 500 ml - Inkspire

€90.28
Tax included
In stock: 2 pz.

Zortrax Gray resin Basic model
If you want information contact the 3dcut specialists !!

Quantity
Last items in stock

Zortrax resin for 3D printing with low shrinkage and short curing time. Perfect for highly detailed display models.

  • Container: bottle

  • Net weight: 500 ml ± 5%

  • Wavelength: 405 nm

Epoxy based resin for 3D printing

Zortrax Resin BASIC is an epoxy-based resin that offers sharp edges, high details and short hardening times. It is durable and easy to print. It is available in gray, white and without pigments. Zortrax Resin BASIC does not contain volatile organic compounds, so it is safe to print according to our safety instructions. The already vulcanized resin is easy to paint.

This resin has a very low shrinkage. Its hardness on the ground is 82.2 D for the pigment-free version and up to 88 D for the white and gray versions. Thanks to its composition, Zortrax Resin BASIC offers smooth surfaces. It can be cured with UV light with a wavelength of 405 nm.

Main features:

  • Low shrinkage

  • Easy to paint

  • Safe for health and the environment

Applications

  • Enclosures for electronics

  • Functional prototypes

  • Exhibition models

  • Parts for end use

  • Translucent models (only without pigments)

Dedicated to

Container

Net weight

Wavelength

 

Zortrax Inkspire

bottle

500 ml ± 5%

405 nm

 

 

 

 

 

 

 

White ivory; Grey

 

without pigment

 

Mechanical properties

metric

Imperial

metric

Imperial

Tensile strength

36 -52 MPa

5220 - 7540 psi

35.7 MPa

5180 psi

Tension module

1,779 - 2,385 GPa

258 - 346 ksi

-

-

Elongation at break

11-20%

11-20%

3%

3%

Flexural strength

59 - 70 MPa

8560 - 10200 psi

-

-

Flexion module

1,882 - 2,385 GPa

273 - 346 ksi

1.56 GPa

226 ksi

Izod Impact, notched

44 - 49 J / m

0.824 - 0.918 ft-lb / in

-

-

Other properties

metric

Imperial

metric

Imperial

Viscosity

150-200 mPa * s

0.00313 - 0.00418 lbf-s / ft2

33 - 57 mPa * s

0.000689 - 0.00119 lbf-s / ft2

Density

1.05 - 1.13 g

0.00232 - 0.00249 lbs

-

-

shrinkage

3.72 - 4.24%

3.72 - 4.24%

2% +/- 1%

2% +/- 1%

Shore hardness (D)

88

88

82.2

82.2

Glass transition temperature

100 ° C

212 ° F

-

-

Hot deformation temperature

80 ° C

176 ° F

-

-